P波模量

在线性弹性力学中，P波模量${\displaystyle M}$，或称纵向弹性模量是用于描述各向同性均质材料的弹性模量。

其定义为单轴应变下轴向应力与轴向应变的比：

${\displaystyle \sigma _{zz}=M\epsilon _{zz}}$

而其他所有的应变${\displaystyle \epsilon _{**}}$均为零。

上式等价于

${\displaystyle M=\rho V_{p}^{2}}$

其中${\displaystyle V_{P}}$是P波速度。

参考文献

• G. Mavko, T. Mukerji, J. Dvorkin. The Rock Physics Handbook. Cambridge University Press 2003 (paperback). ISBN 0-521-54344-4

换算公式
均质各向同性线弹性材料具有独特的弹性性质，因此知道弹性模量中的任意两种，就可由下列换算公式求出其他所有的弹性模量。
	${\displaystyle (\lambda ,\,G)}$	${\displaystyle (E,\,G)}$	${\displaystyle (K,\,\lambda )}$	${\displaystyle (K,\,G)}$	${\displaystyle (\lambda ,\,\nu )}$	${\displaystyle (G,\,\nu )}$	${\displaystyle (E,\,\nu )}$	${\displaystyle (K,\,\nu )}$	${\displaystyle (K,\,E)}$	${\displaystyle (M,\,G)}$
${\displaystyle K=\,}$	${\displaystyle \lambda +{\tfrac {2G}{3}}}$	${\displaystyle {\tfrac {EG}{3(3G-E)}}}$			${\displaystyle {\tfrac {\lambda (1+\nu )}{3\nu }}}$	${\displaystyle {\tfrac {2G(1+\nu )}{3(1-2\nu )}}}$	${\displaystyle {\tfrac {E}{3(1-2\nu )}}}$			${\displaystyle M-{\tfrac {4G}{3}}}$
${\displaystyle E=\,}$	${\displaystyle {\tfrac {G(3\lambda +2G)}{\lambda +G}}}$		${\displaystyle {\tfrac {9K(K-\lambda )}{3K-\lambda }}}$	${\displaystyle {\tfrac {9KG}{3K+G}}}$	${\displaystyle {\tfrac {\lambda (1+\nu )(1-2\nu )}{\nu }}}$	${\displaystyle 2G(1+\nu )\,}$		${\displaystyle 3K(1-2\nu )\,}$		${\displaystyle {\tfrac {G(3M-4G)}{M-G}}}$
${\displaystyle \lambda =\,}$		${\displaystyle {\tfrac {G(E-2G)}{3G-E}}}$		${\displaystyle K-{\tfrac {2G}{3}}}$		${\displaystyle {\tfrac {2G\nu }{1-2\nu }}}$	${\displaystyle {\tfrac {E\nu }{(1+\nu )(1-2\nu )}}}$	${\displaystyle {\tfrac {3K\nu }{1+\nu }}}$	${\displaystyle {\tfrac {3K(3K-E)}{9K-E}}}$	${\displaystyle M-2G\,}$
${\displaystyle G=\,}$			${\displaystyle {\tfrac {3(K-\lambda )}{2}}}$		${\displaystyle {\tfrac {\lambda (1-2\nu )}{2\nu }}}$		${\displaystyle {\tfrac {E}{2(1+\nu )}}}$	${\displaystyle {\tfrac {3K(1-2\nu )}{2(1+\nu )}}}$	${\displaystyle {\tfrac {3KE}{9K-E}}}$
${\displaystyle \nu =\,}$	${\displaystyle {\tfrac {\lambda }{2(\lambda +G)}}}$	${\displaystyle {\tfrac {E}{2G}}-1}$	${\displaystyle {\tfrac {\lambda }{3K-\lambda }}}$	${\displaystyle {\tfrac {3K-2G}{2(3K+G)}}}$					${\displaystyle {\tfrac {3K-E}{6K}}}$	${\displaystyle {\tfrac {M-2G}{2M-2G}}}$
${\displaystyle M=\,}$	${\displaystyle \lambda +2G\,}$	${\displaystyle {\tfrac {G(4G-E)}{3G-E}}}$	${\displaystyle 3K-2\lambda \,}$	${\displaystyle K+{\tfrac {4G}{3}}}$	${\displaystyle {\tfrac {\lambda (1-\nu )}{\nu }}}$	${\displaystyle {\tfrac {2G(1-\nu )}{1-2\nu }}}$	${\displaystyle {\tfrac {E(1-\nu )}{(1+\nu )(1-2\nu )}}}$	${\displaystyle {\tfrac {3K(1-\nu )}{1+\nu }}}$	${\displaystyle {\tfrac {3K(3K+E)}{9K-E}}}$