Zirconium diboride
Chemical compound / From Wikipedia, the free encyclopedia
Dear Wikiwand AI, let's keep it short by simply answering these key questions:
Can you list the top facts and stats about Zirconium diboride?
Summarize this article for a 10 year old
Zirconium diboride (ZrB2) is a highly covalent refractory ceramic material with a hexagonal crystal structure. ZrB2 is an ultra-high temperature ceramic (UHTC) with a melting point of 3246 °C. This along with its relatively low density of ~6.09 g/cm3 (measured density may be higher due to hafnium impurities) and good high temperature strength makes it a candidate for high temperature aerospace applications such as hypersonic flight or rocket propulsion systems. It is an unusual ceramic, having relatively high thermal and electrical conductivities, properties it shares with isostructural titanium diboride and hafnium diboride.
Names | |
---|---|
IUPAC name
Zirconium diboride | |
Other names
ZrB2 | |
Identifiers | |
ECHA InfoCard | 100.031.772 |
PubChem CID |
|
CompTox Dashboard (EPA) |
|
| |
Properties | |
ZrB2 | |
Molar mass | 112.85 g/mol |
Appearance | grey-black powder |
Density | 6.085 g/cm3 |
Melting point | ~3246 °C |
Insoluble | |
Structure | |
Hexagonal, hP3 | |
P6/mmm, No. 191 | |
Hazards | |
Occupational safety and health (OHS/OSH): | |
Main hazards |
Uninvestigated |
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|
ZrB2 parts are usually hot pressed (pressure applied to the heated powder) and then machined to shape. Sintering of ZrB2 is hindered by the material's covalent nature and presence of surface oxides which increase grain coarsening before densification during sintering. Pressureless sintering of ZrB2 is possible with sintering additives such as boron carbide and carbon which react with the surface oxides to increase the driving force for sintering but mechanical properties are degraded compared to hot pressed ZrB2.[2]
Additions of ~30 vol% SiC to ZrB2 is often added to ZrB2 to improve oxidation resistance through SiC creating a protective oxide layer - similar to aluminium's protective alumina layer.[3]
ZrB2 is used in ultra-high temperature ceramic matrix composites (UHTCMCs).[4][5][6][7][8][9][10][11]
Carbon fiber reinforced zirconium diboride composites show high toughness while silicon carbide fiber reinforced zirconium diboride composites are brittle and show a catastrophic failure.