Brucite

Not to be confused with Brushite or Brucine.

Brucite is the mineral form of magnesium hydroxide, with the chemical formula Mg(OH)₂. It is a common alteration product of periclase in marble; a low-temperature hydrothermal vein mineral in metamorphosed limestones and chlorite schists; and formed during serpentinization of dunites. Brucite is often found in association with serpentine, calcite, aragonite, dolomite, magnesite, hydromagnesite, artinite, talc and chrysotile.

Brucite
General
Category	Oxide mineral
Formula	Mg(OH)2
IMA symbol	Brc[1]
Strunz classification	4.FE.05
Crystal system	Trigonal
Crystal class	Hexagonal crystal family (3m) H-M symbol: (3 2/m)
Space group	P3m1
Unit cell	a = 3.142(1) Å, c = 4.766(2) Å; Z = 1
Identification
Color	White, pale green, blue, gray; honey-yellow to brownish red
Crystal habit	Tabular crystals; platy or foliated masses and rosettes – fibrous to massive
Cleavage	Perfect on {0001}
Fracture	Irregular
Tenacity	Sectile
Mohs scale hardness	2.5 to 3
Luster	Vitreous to pearly
Streak	White
Diaphaneity	Transparent
Specific gravity	2.39 to 2.40
Optical properties	Uniaxial (+)
Refractive index	nω = 1.56–1.59 nε = 1.58–1.60
Birefringence	0.02
Other characteristics	Pyroelectric
References	[2][3][4]

It adopts a layered CdI₂-like structure with hydrogen-bonds between the layers.^[5]

Discovery

Brucite was first described in 1824 by François Sulpice Beudant^[6] and named for the discoverer, American mineralogist, Archibald Bruce (1777–1818). A fibrous variety of brucite is called nemalite. It occurs in fibers or laths, usually elongated along [1010], but sometimes [1120] crystalline directions.

Occurrence

A notable location in the US is Wood's Chrome Mine, Cedar Hill Quarry, Lancaster County, Pennsylvania. Yellow, white and blue brucite with a botryoidal habit was discovered in Qila Saifullah District of Province Baluchistan, Pakistan. In a later discovery, brucite also occurred in the Bela Ophiolite of Wadh, Khuzdar District, Province Baluchistan, Pakistan. Brucite has also occurred from South Africa, Italy, Russia, Canada, and other localities as well, but the most notable discoveries are the US, Russian and Pakistani examples.^{[citation needed]}

Industrial applications

Synthetic brucite is mainly consumed as a precursor to magnesia (MgO), a useful refractory and thermal insulator. It finds some use as a flame retardant because it thermally decomposes to release water in a similar way to aluminium hydroxide (Al(OH)₃) and mixtures of huntite (Mg₃Ca(CO₃)₄) and hydromagnesite (Mg₅(CO₃)₄(OH)₂·4H₂O).^[7][8] It also constitutes a significant source of magnesium for industry. Although generally deemed safe, brucite can be contaminated with naturally occurring asbestos fibers.^[9]

Degradation of cement and concrete

When cement or concrete are exposed to Mg²⁺ and SO2−4 ions simultaneously present in seawater, the precipitation of the poorly soluble brucite contributes to enhance the formation of gypsum in the sulfate attack :

MgSO₄ + Ca(OH)₂ + 2 H₂O → Mg(OH)₂ + CaSO₄ · 2H₂O

The precipitation of insoluble Mg(OH)₂ helps to considerably drive the chemical equilibrium of the reaction to the right. It exacerbates the sulfate attack resulting in the formation of gypsum and ettringite (an expansive phase) responsible for the mechanical stress in the hardened cement paste. However, brucite, a phase with a small molar volume (24.63 cm³/mol),^[10] may contribute to clogging the porous network in the hardened cement paste, hindering the diffusion of these harmful reactive species in the cement matrix. This can delay the decalcification of the C-S-H phase (the "glue" phase in the hardened cement paste responsible for the cohesion in concrete) and its transformation into an M-S-H phase.

The exact mechanism of brucite degradation of hardened cement paste remains a matter of debate.^[11] If brucite had a high molar volume, it could be de facto considered a swelling phase (like ettringite, or highly hydrated minerals), but this does not appear to be the case. It is unclear if it causes expansion or not, and how. If it replaces another phase locally (topo chemical replacement), in cases where its molar volume is smaller than that of the phase it replaces, no expansion is expected; rather, a decrease in porosity is anticipated. However, if it crystallizes in a large number of tiny crystals growing between existing ones, even with a small molar volume, it could exert a considerable crystallization pressure in the cement matrix, resulting in tensile stress, expansion and cracking.

Anyway, prolonged contact between seawater, or naturally rich Mg-brines, and concrete may induce durability issues for regularly immersed concrete structures, and their components, especially if they also contain steel reinforcements (pitting corrosion caused by chloride ions).

The use of dolomite as aggregate in concrete made with a cement with a too high alkali content can also cause brucite precipitation, driving the dedolomitization reaction, as observed in the alkali-aggregate reaction.^[12]

Ca,Mg(CO₃)₂ + 2 NaOH → Mg(OH)₂ + CaCO₃ + Na₂CO₃

Consequently, the use of dolomite is prohibited as aggregate for concrete.

Gallery

• 
  Yellow brucite from Balochistan, Pakistan
• 
  Nemalite
• 
  Brucite crystals from the Sverdlovsk Region, Urals, Russia (size: 10.5 x 7.8 x 7.4 cm)
• 
  Structure of Mg(OH)₂

See also

• List of minerals
• List of minerals named after people
• Portlandite, Ca(OH)₂
• Cookeite, LiAl₄(Si₃Al)O₁₀(OH)₈