Process of layering steel or iron with zinc to prevent rusting From Wikipedia, the free encyclopedia
Remove ads
Galvanization (also spelled galvanisation)[1] is the process of applying a protective zinc coating to steel or iron, to prevent rusting. The most common method is hot-dip galvanizing, in which the parts are coated by submerging them in a bath of hot, molten zinc.[2]
Galvanized steel is widely used in applications where corrosion resistance is needed without the cost of stainless steel, and is considered superior in terms of cost and life-cycle. It can be identified by the crystallization patterning on the surface (often called a "spangle").[3]
Galvanized steel can be welded; however, welding gives off toxic zinc fumes. Galvanized fumes are released when the galvanized metal reaches a certain temperature. This temperature varies by the galvanization process used. In long-term, continuous exposure, the recommended maximum temperature for hot-dip galvanized steel is 200 °C (392 °F), according to the American Galvanizers Association. The use of galvanized steel at temperatures above this will result in peeling of the zinc at the inter-metallic layer.[4]
Like other corrosion protection systems, galvanizing protects steel by acting as a barrier between steel and the atmosphere. However, zinc is a more electropositive (active) metal in comparison to steel. This is a unique characteristic for galvanizing, which means that when a galvanized coating is damaged and steel is exposed to the atmosphere, zinc can continue to protect steel through galvanic corrosion (often within an annulus of 5 mm, above which electron transfer rate decreases).
Remove ads
History and etymology
The process is named after the Italian physician, physicist, biologist and philosopher Luigi Galvani (9 September 1737 – 4 December 1798). The earliest known example of galvanized iron was discovered on 17th-century Indian armour in the Royal Armouries Museum collection in the United Kingdom.[5]
The term "galvanized" can also be used metaphorically of any stimulus which results in activity by a person or group of people.[6]
In modern usage, the term "galvanizing" has largely come to be associated with zinc coatings, to the exclusion of other metals. Galvanic paint, a precursor to hot-dip galvanizing, was patented by Stanislas Sorel, of Paris, on June 10, 1837, as an adoption of a term from a highly fashionable field of contemporary science, despite having no evident relation to it.[7]
Remove ads
Principle
The zinc coating, when intact, prevents corrosive substances from reaching the underlying iron.[8] It's main function is to act as a sacrificial anode to prevent the iron from rusting by cathodic protection. Zinc is more reactive than iron, so the zinc coating preferentially oxidizes to zinc carbonate, preventing the iron from corroding, even if there are gaps in the zinc coating. Additional electroplating such as a chromate conversion coating may be applied to provide further surface passivation to the substrate material.[9]
Remove ads
Corrosion
Galvanized steel can last for many decades if other supplementary measures are maintained, such as paint coatings and additional sacrificial anodes. Corrosion in non-salty environments is caused mainly by levels of sulfur dioxide in the air.[10]
Methods
Hot-dip galvanizing deposits a thick, robust layer of zinc iron alloys on the surface of a steel item. The hot-dip process generally does not reduce strength to a measurable degree, with the exception of high-strength steels where hydrogen embrittlement can become a problem.[11]
Galvanization can be done using electricity in electrogalvanization.
Sherardizing provides a zinc diffusion coating on iron- or copper-based materials.[12][13]
Remove ads
Common use
Summarize
Perspective
Construction steel
This is the most common use for galvanized metal; hundreds of thousands of tons of steel products are galvanized annually worldwide. In developed countries, most larger cities have several galvanizing factories, and many items of steel manufacture are galvanized for protection. Typically these include street furniture, building frameworks, balconies, verandahs, staircases, ladders, walkways, and more. Hot dip galvanized steel is also used for making steel frames as a basic construction material for steel frame buildings.[14]
Piping
In the early 20th century, galvanized piping swiftly took the place of previously used cast iron and lead in cold-water plumbing. Galvanized piping rusts from the inside out, building up layers of plaque on the inside of the piping, causing both water pressure problems and eventual pipe failure. These plaques can flake off, leading to visible impurities in water and a slight metallic taste. The life expectancy of galvanized piping is about 40–50 years,[15] but it may vary on how well the pipes were built and installed. Pipe longevity also depends on the thickness of zinc in the original galvanizing, which ranges on a scale from G01 to G360.[16]
Automotive
In the case of automobile bodies, where additional decorative coatings of paint will be applied, a thinner form of galvanizing is applied by electrogalvanizing. Electrogalvanized sheet steel is often used in automotive manufacturing to enhance the corrosion performance of exterior body panels; this tends to achieve lower coating thicknesses of zinc compared to hot-dip galvanization.